Nickel aluminum bronze

C63200 characteristics: good heat workability. C63200 aluminum bronze is mainly used as bar, forgings, bolts, nuts, pump parts, corrosion resistant parts.

Name

Copper or copper alloy UNS number

Main chemical composition,%

Copper or copper alloy UNS number

Name

Recommended casting temperature

Forging rating A.

Copper

Lead

Iron

Nickel (cobalt)

Aluminium

Silicon

Manganese

≥of specified range elements + copper

°F

K

Aluminum nickel Bronze

C63200

Residual residue

≤0.02

E 3.5-4.3

4.0-4.8

8.7-9.5

≤0.10

1.2-2.0

99.5

C63200

Aluminum nickel bronze

1450-1700

1060-1200

75


China

ISO of international standards

Former Soviet Union

United States (SYMBOL)

Japan

Germany

Britain

France

...

CuAl10Ni

...

C63200

...

CW307G

CA104

...


C95500 characteristics: good cutting ability, good mechanical properties, can withstand cold. Hot pressure processing, easy welding, brazing well, good stability to general corrosion, but there is a tendency of corrosion and rupture, mainly used in air conditioning valves, hardware machinery and so on.

Name

Copper alloy UNS number

Main chemical composition/%

Category

Copper alloy UNS number

Ksi[Mpa] of minimum tensile strength

Minimum yield strength Ksi[Mpa]

Extensions from 2 inches [50.08 mm],%

Bush Hardness (Load 3000- kg)

Copper

Aluminium

Titanium

Manganese

Nickel (including cobalt)

Nickel aluminium Bronze

C95500

≥78.0

10.0-11.5

3.0-5.0

≤3.5

3.0-5.5

Nickel aluminum bronze

as cast

C95500

90[620]

40[275]

6

190


Heat treatment

Solution treatment (not less than 1 hour followed by water quenching)

Annealing (not less than 1 hour after air cooling)

1600-1700°F [870-925℃]

925-1000°F [495-540℃]


China

ISO of international standards

Former Soviet Union

United States (SYMBOL)

Japan

Germany

Britain

France

...

CuAl10Fe5Ni5-C


C95500


CC333G

AB2-C




C95520 characteristics: high mechanical properties, good corrosion resistance in atmosphere, fresh water and seawater, good casting performance, compact alloy structure, high air tightness, good wear resistance, can be welded, not easy to braze. C95520 cast copper alloy for corrosion-resistant, wear-resistant parts, simple shape of large castings

Name

Copper alloy UNS number

Main chemical composition/%

Copper

Aluminium

Titanium

Manganese

Nickel (including cobalt)

Silicon

Lead

Nickel aluminum bronze

C95520A

≥74.5

10.5-11.5

4.0-5.5

≤1.5

4.2-6.0

≤0.15

≤0.03


Heat treatment

Solution treatment (not less than 1 hour followed by water quenching)

Annealing (not less than 1 hour after air cooling)

              1600-1700°F [870-925℃]

             925-1000°F [495-540℃]


C95600 features: with good cutting grinding performance, can be welded, easy to hot machining molding. Aluminum bronze is mainly used to make high strength and wear-resistant structural parts such as support, gear, shaft sleeve, bushing, nozzle, flange, rocker arm, guide valve, pump rod, cam, fixed nut, etc.

Name

Copper alloy UNS number

Main chemical composition/%

Copper alloy UNS number

Ksi[Mpa] of minimum tensile strength

Minimum yield strength Ksi[Mpa]

Extensions from 2 inches [50.08 mm],%

Copper

Aluminium

Nickel (including cobalt)

Silicon

Silicon aluminum bronze

C95600

≥88.0

6.0-8.0

≤0.25

1.8-3.2

C95600

60[415]

28[195]

10



C95700 features:: high mechanical properties, good wear resistance and corrosion resistance, can be welded, not easy to braze, large castings since 700℃ air cooling can prevent brittle.

Name

Copper alloy UNS number

Main chemical composition/%

Copper alloy UNS number

Ksi[Mpa] of minimum tensile strength

Minimum yield strength Ksi[Mpa]

Extensions from 2 inches [50.08 mm],%

Copper

Aluminium

Titanium

Manganese

Nickel (including cobalt)

Silicon

Lead

Manganese Nickel Aluminum Bronze

C95700

≥71.0

7.0-8.5

2.0-4.0

11.0-14.0

1.5-3.0

≤0.10

≤0.03

C95700

90[620]

40[275]

20


China

ISO of international standards

Former Soviet Union

United States (SYMBOL)

Japan

Germany

Britain

France

ZCuAl8Mn13Fe3Ni2

...

HBBa-70

C95700

ALBC4

Al-MnBZ13

CMA1

...



C95800 characteristics: aluminum bronze containing iron and manganese elements, belonging to high strength heat resistant bronze, stable mechanical properties at high temperature (400℃), good friction reduction, good corrosion resistance in atmosphere, fresh water and sea water, good pressure processing under hot state, heat treatment strengthening, welding, not easy fiber welding, good cutting performance.

Name

Copper alloy UNS number

Main chemical composition/%

Copper alloy UNS number

Ksi[Mpa] of minimum tensile strength

Minimum yield strength Ksi[Mpa]

Extensions from 2 inches [50.08 mm],%

Bush Hardness (Load 3000- kg)

Copper

Aluminium

Titanium

Manganese

Nickel (including cobalt)

Silicon

Lead

Nickel aluminum bronze

C95800

≥79.0

8.5-9.5

C 3.5-4.5

0.8-1.5

4.0-5.0

≤0.10

≤0.03

C95800

85[585]

35[240]

15

...


China

ISO of international standards

Former Soviet Union

United States (SYMBOL)

Japan

Germany

Britain

France

ZCuAl9Fe4Ni4Mn2

...

BPAЖHMЦ(9-4-4-1)

C95800

ALBC3

...

AB2

CuAl10Fe5Ni5


Name

Copper alloy UNS number

Main chemical composition/%

Category

Copper alloy UNS number

Ksi[Mpa] of minimum tensile strength

Minimum yield strength Ksi[Mpa]

Extensions from 2 inches [50.08 mm],%

Copper

Aluminium

Titanium

Manganese

Nickel (including cobalt)

Silicon

C95820B

≥77.5

9.0-10.0

4.0-5.0

≤1.5

4.5-5.8

≤0.10

≤0.02

Nickel aluminum bronze

as cast

C95820

94[650]

39[270]

13